KINETICS OF SOLID-STATE MULLITE SYNTHESIS FROM ACTIVATED PRECURSORS

The solid-state synthesis kinetics of the mullite 3Al2O3∙2SiO2 from aluminium hydroxide and metasilicic acid was studied. Hydrated oxides obtained in an active form as a result of a mechanical acti-vation or co-precipitation (precursors) were subjected to a high-temperature treatment. The reaction rate was described by the kinetic first-order equation. Effective rate constants and energy activation were de-termined. The positive action of mullite seed crystals on the product accumulation was confirmed.
Key words: mullite, solid-state synthesis, kinetics, precursors, mechanical activation, co-precipitation, seed crystals

2016, Т. 59, № 1, Стр. 36-38

КИНЕТИКА ТВЕРДОФАЗНОГО СИНТЕЗА МУЛЛИТА ИЗ АКТИВИРОВАННЫХ ПРЕКУРСОРОВ

Изучена кинетика твердофазного синтеза муллита 3Al2O3∙2SiO2 из гидроксида алюминия и метакремниевой кислоты. Гидратированные оксиды, полученные в активной форме в результате механической активации или совместного осаждения (прекурсоры), подвергали высокотемпературной обработке. Скорость реакции описана кинетическим уравнением первого порядка. Определены величины эффективных констант скорости и энергии активации.

2016, Т. 59, № 1, Стр. 36-38

ТЕРМИЧЕСКИЙ АНАЛИЗ ТЕТРА(ИЗОТИОЦИАНАТО)ДИАМИНХРОМАТА(III) ДИНИТРАТОТЕТРА(ГЕКСАМЕТИЛФОСФОРТРИАМИД)ЛАНТАНА(III)

Синтезировано координационное соединение
состава [LaL4(NO3)2][Cr(NH3)2(NCS)4],
где L = OP(NMe2)3 и изучена его термическая устойчивость
на воздухе и в инертной атмосфере.

Ключевые слова: редкоземельные элементы, гексаметилфосфортриамид, термогравиметрия

2013, Т. 56, № 10, Стр. 36-38