DOI: 10.6060/tcct.20165911.5463
Izv. Vyssh. Uchebn. Zaved. Khim. Khim. Tekhnol. 2016. V. 59. N 11. P. 70-76

The synthesis processes of the low-modulus granulated zeolites from mixtures of 6Al2Si2O7:12NaOH and 6Al2Si2O7:12NaOH:12SiO2 were studied using ultrasonic treatment of the aqueous suspensions. To control the synthesis processes, X-ray diffraction, scanning electron microscopy and infrared spectroscopy were used. It was shown that after thermal treatment of the mixture of 6Al2Si2O7:12NaOH at 650 °C, SOD zeolite (|Na6|[Al6Si6O24]) and sodium aluminosilicate (Na8Al4Si4O18) are synthesized. The calcination of the mixture of 6Al2Si2O7:12NaOH: 12SiO2 does not result in a formation of new crystalline phases. After the hydrothermal crystallization of the mixture of 6Al2Si2O7:12NaOH in 2M NaOH solution LTA zeolite (|Na12|[Al12Si12O48]) is synthesized. It was established that Na8Al4Si4O18 is a precursor of LTA zeolite. Hydrothermal crystallization of the mixture with SiO2 excess in 2M NaOH so-lution results in a formation of zeolite PHI (|Na6|[Al6Si10O32]). It has been shown that after crystallization of the both mixtures in 6M NaOH solution, only SOD zeolite is the final prod-uct of the synthesis.

Key words: synthesis, SOD zeolite, LTA zeolite, PHI zeolite


1. Breck D. Zeolite Molecular Sieves. Structure, chemistry and use. New York: Wiley. 1974. 781 p.
2. Johnson E.B.G., Arshad S.E. Appl. Clay Sci. 2014. V. 97–98. P. 215–221.
3. Ríos C.A., Williams C.D., Fullen M.A. Appl. Clay Sci. 2009. V. 42. P. 446–454.
4. Pavlov M.L., Travkina O.S., Basimova R.A., Pavlova I.N., Kutepov B.I. Petrol. Chem. 2009. V. 49. N 1. P. 36-41.
5. Kuttruff H. Ultrasonics fundamentals and applications. London: Elsevier Science Publishers. 1991. 495 p.
6. Gandhi K.S., Kumar R. Sadhana. 1994. V. 19. N 6. P. 1055–1076.
7. Askari S., Alipour Sh.M., Halladj R., Farahani M.H.D.A. J. Porous Mater. 2013. V. 20. N 1. P. 285–302.
8. Gordina N.E., Prokof’ev V.Yu., Kul’pina Yu.N., Petuhova N.V., Gazahova S.I., Hmylova O.E. Ultrason. Sonochem. 2016. V. 33. P. 210–219.
9. Prokof’ev V.Yu., Gordina N.E., Zhidkova A.B., Efremov A.M. J. Mater. Sci. 2012. V. 47. N 14. P. 5385–5392.
10. Prokof'ev V.Yu., Gordina N.E. Appl. Clay Sci. 2014. V. 101. P. 44–51.
11. Prokof’ev V.Yu., Gordina N.E., Zhidkova A.B. Russ. J. Appl. Chem. 2012. V. 85. N 7. P. 1077–1082.
12. Thomas J.M., Vaughan D.E.W. J. Phys. Chem. Solids. 1989. V. 50. N 5. P. 449–467.
13. Giacovazzo C., Monaco H.L., Viterbo D., Scordari F., Gilli G., Zanotti G., Catti M. Fundamentals of Crystallo-graphy. Oxford: Oxford University Press. 1992. 682 p.
14. Karge H.G., Weitkamp J. Molecular Sieves – Science and Technology. V. 4. Char. I. Berlin: Springer-Verlag. 2004. 625 p.

2016, Т. 59, № 11, Стр. 70-76


You will get the pdf-copy of your article by e-mail