The process of calcium ferrite preparing from ferrum (II) oxalate and calcium hy-droxide by solid-phase interaction was studied using data of X-ray diffraction, X-ray phase analysis, simultaneous thermal analysis, and scanning electron microscopy. X-ray phase analysis results of a sample subjected to heat treatment at 750 °C for 3 h, show formation of single-phase brownmillerite structure of calcium ferrite Ca2Fe2O5. Analysis of the DTA shows that crystallization process continues up to 1000 °C. Calculation of substructure parameters of Ca2Fe2O5 shows that the area of coherent X-ray scattering is 198 Ǻ, total amount of mi-crostrains is 0.8 %. The specific surface area of the sample is not more 5 m2/g.

Key words: calcium ferrite, solid phase synthesis, brownmillerite structure

1. Tejuca L.G., Fierro J.L.G., Tascón J.M.D. Structure and Reactivity of Perovskite-Type Oxides. Advances in catalysis. 1989. V. 36. P. 237-328.
2. Isupova L.A., Tsybulya S.V., Kryukova G.N. Mechanochemical synthesis and catalytic properties of the calcium ferrite Ca2Fe2O5. Kinetics and Catalysis. 2002. V. 43. N 1. P. 122-128.
3. Rumyantsev R.N., Kochetkov S.P., Lapshin M.A. Influence of calcium and copper ferrites on activity and selectivity of the medium temperature CO conversion catalysts. Izv. Vyssh. Uchebn. Zaved. Khim. Khim. Tekhnol. 2016. V. 59. N 3. P. 43-48 (in Russian).
4. Il'in A.A., Il'in A.P., Kurochkin V. Yu., Smirnov N.N. Mechanochemical synthesis of medium temperature conversion of car-bon monoxide catalyst by water vapour. Uspehi v khimii i khimicheskoiy tekhnologii. 2007. V. XXI. N 9 (77). P. 79-83 (in Rus-sian).
5. Isupova L.A., Yakovleva I.S., Сybulja S.V. Mechanochemical synthesis method of perovskite catalysts La1-хCaXFeO3-0.5X for oxidizing catalytic processes. Khimiya v interesakh ustoiychivogo razvitiya. 2002. V. 10. N 1-2. P. 77-78 (in Russian).
6. Rumyantsev R.N., Il’in A.A., Babichev I.V., Il’in A.P. Decomposition of nitric oxide(I) on the ferrite with different crystal structures. SITA-Journal. 2014. V. 16. N 3. P. 1-5.
7. Hasmonay Е., Depeyrot J., Sousa М.Н. Magnetic and optical properties of ionic ferrofluids based on nickel ferrite nanoparticles. J. Appl. Phys. 2000. V. 88. N 11. P. 6628- 6635.
8. Tartaj P., Morales M.P., Veintemillas-Verdaguer S. The preparation of magnetic nanoparticles for applications inbiomedicine. J. Phys. D: Appl. Phys. 2003. V. 36. P. 182-197.
9. Gubkin S.P., Koksharov Yu.A., Khomutov G.B., Yurkov G.U. Magnetic nanoparticles: preparation, structure and properties. Russian Chemical Reviews. 2005. V. 74. N 6. P. 489-520.

2016, Т. 59, № 12, Стр. 45-48


You will get the pdf-copy of your article by e-mail